SS 316 / 316L Flanges
Teshi Group manufactures SS 316 / 316L flanges (ASTM A182 F316 / F316L, UNS S31600 / S31603, 1.4401 / 1.4404) as an OEM in India — forged, machined, marked and certified in-house to ASME B16.5, ASME B16.47, EN 1092-1 and customer drawings.
Austenitic stainless steels are the everyday choice for corrosive process lines, with grades tuned for low carbon (L), molybdenum for chlorides (316, 317L), stabilisation for high temperature (321, 347) and oxidation resistance (310).
SS 316 / 316L flanges at a glance
| Material | SS 316 / 316L |
|---|---|
| Specification | ASTM A182 F316 / F316L |
| UNS / W.Nr. | S31600 / S31603 / 1.4401 / 1.4404 |
| Sizes | NPS ½"–24" (ASME B16.5), 26"–60" (ASME B16.47 A / B), DN 10–600 (EN 1092-1) |
| Pressure class | Class 150, 300, 600, 900, 1500, 2500 · PN 6–40 |
| Facing / ends | RF, FF, RTJ, tongue & groove, male-female; serrated or smooth finish |
| Certification | EN 10204 3.1 standard · 3.2 with third-party inspection · IBR on request |
| Testing | PMI, hardness, dimensional; UT, IGC, impact and ferrite as specified |
SS 316 / 316L chemistry and mechanical properties
Chemical composition of SS 316 / 316L (weight %, maximum unless a range)
| Grade | C | Mn | Si | Cr | Ni | Mo |
|---|---|---|---|---|---|---|
| 316 / 316L | 0.08 / 0.030 | 2.00 | 1.00 | 16.0–18.0 | 10.0–14.0 | 2.00–3.00 |
Mechanical properties of SS 316 / 316L (minimum, room temperature)
| Grade | Tensile strength | Yield strength (0.2 %) | Elongation | Note |
|---|---|---|---|---|
| 316 / 316L | 515 MPa (75 ksi) | 205 MPa (30 ksi) | 30 % | 316L: 485 / 170 MPa |
Matching specifications by product form
| Grade | Forged flanges & fittings | Butt weld fittings | Plate | Pipe |
|---|---|---|---|---|
| 316 / 316LUNS S31600 / S31603 · W.Nr. 1.4401 / 1.4404 | ASTM A182 F316 / F316L | ASTM A403 WP316 / WP316L | ASTM A240 | ASTM A312 |
Limits and minimums from the governing ASTM / ASME specifications, summarised for convenience; the current edition takes precedence.
Pressure rating
Pressure–temperature ratings of SS 316 / 316L flanges to ASME B16.5 (bar, gauge). Ratings apply to the flange; the joint rating also depends on bolting and gasket.
Material Group 2.2: A182 F316 / F316H
| Temp.°C | Class 150bar | Class 300bar | Class 600bar | Class 900bar | Class 1500bar | Class 2500bar |
|---|---|---|---|---|---|---|
| −29 to 38 | 19.0 | 49.6 | 99.3 | 148.9 | 248.2 | 413.7 |
| 50 | 18.4 | 48.1 | 96.2 | 144.3 | 240.6 | 400.9 |
| 100 | 16.2 | 42.2 | 84.4 | 126.6 | 211.0 | 351.6 |
| 150 | 14.8 | 38.5 | 77.0 | 115.5 | 192.5 | 320.8 |
| 200 | 13.7 | 35.7 | 71.3 | 107.0 | 178.3 | 297.2 |
| 250 | 12.1 | 33.4 | 66.8 | 100.1 | 166.9 | 278.1 |
| 300 | 10.2 | 31.6 | 63.2 | 94.9 | 158.1 | 263.5 |
| 325 | 9.3 | 30.9 | 61.8 | 92.7 | 154.4 | 257.4 |
| 350 | 8.4 | 30.3 | 60.7 | 91.0 | 151.6 | 252.7 |
| 375 | 7.4 | 29.9 | 59.8 | 89.6 | 149.4 | 249.0 |
| 400 | 6.5 | 29.4 | 58.9 | 88.3 | 147.2 | 245.3 |
| 425 | 5.5 | 29.1 | 58.3 | 87.4 | 145.7 | 242.9 |
| 450 | 4.6 | 28.8 | 57.7 | 86.5 | 144.2 | 240.4 |
| 475 | 3.7 | 28.7 | 57.3 | 86.0 | 143.4 | 238.9 |
| 500 | 2.8 | 28.2 | 56.5 | 84.7 | 140.9 | 235.0 |
| 538 | 1.4 | 25.2 | 50.0 | 75.2 | 125.5 | 208.9 |
Material Group 2.3: A182 F304L / F316L
| Temp.°C | Class 150bar | Class 300bar | Class 600bar | Class 900bar | Class 1500bar | Class 2500bar |
|---|---|---|---|---|---|---|
| −29 to 38 | 15.9 | 41.4 | 82.7 | 124.1 | 206.8 | 344.7 |
| 50 | 15.3 | 40.0 | 80.0 | 120.1 | 200.1 | 333.5 |
| 100 | 13.3 | 34.8 | 69.6 | 104.4 | 173.9 | 289.9 |
| 150 | 12.0 | 31.4 | 62.8 | 94.2 | 157.0 | 261.6 |
| 200 | 11.2 | 29.2 | 58.3 | 87.5 | 145.8 | 243.0 |
| 250 | 10.5 | 27.5 | 54.9 | 82.4 | 137.3 | 228.9 |
| 300 | 10.0 | 26.1 | 52.1 | 78.2 | 130.3 | 217.2 |
| 325 | 9.3 | 25.5 | 51.0 | 76.4 | 127.4 | 212.3 |
| 350 | 8.4 | 25.1 | 50.1 | 75.2 | 125.4 | 208.9 |
| 375 | 7.4 | 24.8 | 49.5 | 74.3 | 123.8 | 206.3 |
| 400 | 6.5 | 24.3 | 48.6 | 72.9 | 121.5 | 202.5 |
| 425 | 5.5 | 23.9 | 47.7 | 71.6 | 119.3 | 198.8 |
| 450 | 4.6 | 23.4 | 46.8 | 70.2 | 117.1 | 195.1 |
Types we manufacture
Dimension charts
Where SS 316 / 316L is used
- Chemical, fertiliser and pharmaceutical process piping
- Food, water and utility lines
- Refinery hydrotreater and high-temperature lines (321, 347)
- Furnace and kiln piping (310S)
- Cryogenic service
Testing & certification
- Solution annealed
- Intergranular corrosion test to ASTM A262 Practice E when specified
- PMI and dimensional inspection
- EN 10204 3.1 certificate
Related materials
FAQ
SS 316 / 316L flanges: common questions
What specification covers SS 316 / 316L flanges?
SS 316 / 316L flanges are forged to ASTM A182 F316 / F316L and dimensioned to ASME B16.5, ASME B16.47 or EN 1092-1.
What is the chemical composition of 316 / 316L?
316 / 316L (UNS S31600 / S31603): C 0.08 / 0.030, Mn 2.00, Si 1.00, Cr 16.0–18.0, Ni 10.0–14.0, Mo 2.00–3.00 (weight %; single values are maximums).
What are the minimum mechanical properties of 316 / 316L?
Tensile strength 515 MPa (75 ksi), yield strength 205 MPa (30 ksi), elongation 30 %.
Is Teshi Group a manufacturer of SS 316 / 316L flanges in India?
Yes. Teshi Group has manufactured flanges and fittings in India since 1971 and is ISO 9001:2015 certified and IBR approved. Every SS 316 / 316L piece is hard-stamped with its heat number and supplied with an EN 10204 3.1 certificate; 3.2 with third-party inspection on request.
What does the L in 304L and 316L mean?
L grades have carbon limited to 0.030 % to avoid chromium carbide precipitation during welding, which protects the weld zone from intergranular corrosion.
When should 321 or 347 be used instead of 304L?
321 (titanium-stabilised) and 347 (niobium-stabilised) resist sensitisation during long service at roughly 425–850 °C, so they are used in refinery hydrotreaters and high-temperature lines.
Austenitic stainless steel grade data sheets
Austenitic stainless steel overview →Chemical composition, mechanical properties and PDF data sheet for each grade.