ASTM A217 WC1 — Chemical Composition & Mechanical Properties
ASTM A217 WC1 is a chrome-moly alloy steel grade for alloy steel castings (UNS J12524, EN / W.Nr ≈ 1.5419 (G20Mo5)). It is also known as C-½Mo cast. This sheet summarises its chemical composition limits, minimum mechanical properties, heat treatment and typical service. Teshi Group manufactures valves with bodies in this grade.
ASTM A217 WC1 at a glance
| Specification | ASTM A217 WC1 |
|---|---|
| Material family | Chrome-moly alloy steel |
| Product form | Alloy steel castings |
| UNS number | J12524 |
| EN / W.Nr equivalent | ≈ 1.5419 (G20Mo5) |
| Also known as | C-½Mo cast |
| Document | TG-MG-149 · Rev. 1 · October 2026 |
Typical service
Carbon-moly valve bodies
Heat treatment
Normalised and tempered 595 °C min
Chemical composition of ASTM A217 WC1 (weight %)
Single values are maximums unless shown as a range or “min”.
Mechanical properties
| Tensile strength, min | 450 MPa |
|---|---|
| Yield strength (0.2 % offset), min | 240 MPa |
| Elongation, min | 24 % |
| Tensile strength, max | 620 MPa |
| Hardness | Not specified |
About chrome-moly alloy steel
Chrome-moly steels are low-alloy steels with 1–9 % chromium and 0.5–1 % molybdenum. Chromium gives oxidation and sulphidation resistance; molybdenum gives creep strength at high temperature. They are the standard choice for steam and hot hydrocarbon service above the carbon-steel range.
Reference information compiled from the published standard for convenience. It does not replace the current edition of the governing standard, which takes precedence. Verify critical dimensions and properties before design, purchase or fabrication. Teshi Engineers & Sales Promoters (P) Ltd accepts no liability for errors or omissions.
International equivalents of ASTM A217 WC1
All equivalents| Standard system | Nearest equivalent grade |
|---|---|
| USA — ASTM / ASME | ASTM A217 WC1 · ASME SA-217 WC1 |
| USA — UNS | J12524 |
| Europe — EN designation | G20Mo5 (EN 10213) |
| Europe — W.Nr | 1.5419 |
| Japan — JIS | SCPH11 (JIS G5151) |
| China — GB / NB | WC1 (GB/T 12229) / ZG20Mo |
| UK — BS (withdrawn) | BS 1504-245 |
Equivalents are the nearest commonly cited grades. Chemistry, mechanical properties and testing differ between standards — compare them before substituting one for another.
Standards for ASTM A217 WC1
All material standardsFAQ
ASTM A217 WC1: common questions
What is the minimum yield strength of ASTM A217 WC1?
240 MPa, with a minimum tensile strength of 450 MPa.
What is the carbon content of ASTM A217 WC1?
0.25 max %.
What is the UNS number and EN equivalent of ASTM A217 WC1?
UNS J12524; the nearest European designation is W.Nr ≈ 1.5419 (G20Mo5). Equivalents are close but not identical — check the specification if substituting.
How is ASTM A217 WC1 heat treated?
Normalised and tempered 595 °C min.
What is the Chinese (GB) equivalent of ASTM A217 WC1?
The nearest Chinese equivalent is WC1 (GB/T 12229) / ZG20Mo. Equivalents are close but not identical — compare chemistry and properties before substituting.
What is the JIS equivalent of ASTM A217 WC1?
The nearest Japanese (JIS) equivalent is SCPH11 (JIS G5151).
Does Teshi Group supply ASTM A217 WC1?
Teshi Group manufactures valves with bodies in this grade. Send your size, rating and quantity to info@teshigroup.com for a quotation with EN 10204 3.1 certificates.
Related products, data sheets and standards
Gate Valve
OEM manufacturer
View online · PDFTechnical data sheetGlobe Valve
OEM manufacturer
View online · PDFTechnical data sheetCheck Valve
OEM manufacturer
View online · PDFTechnical data sheetBall Valve
OEM manufacturer
View online · PDFMaterial productsChrome-Moly Alloy Steel Flanges & Fittings — F5 to F91
Grades, sizes and standards we supply
ViewMaterial productsASTM A182 F11 / F22 Alloy Steel Flanges
Grades, sizes and standards we supply
ViewMaterial productsASTM A182 F5 / F9 / F91 Alloy Steel Flanges
Grades, sizes and standards we supply
View
Ready to build to spec?
Share your drawing, bill of materials or technical requirements with the Teshi team.